论文网
电化学有关论文范文素材,与硕士生学位文开题相关毕业论文格式范文
本论文是一篇电化学有关毕业论文格式范文,关于硕士生学位文开题相关毕业论文格式范文。免费优秀的关于电化学及机械电子工程及合金方面论文范文资料,适合电化学论文写作的大学硕士及本科毕业论文开题报告范文和学术职称论文参考文献下载。
cingthesafetyofthewholesystem.Bythesystemexample,theprocessandmethodofusingthesystemispresented.Ithasimportantsignificancetocreatingthedatamanagementsystemorientedtoproductdevelopingprocessbasedonthewebforthedigitalizationofthebusenterprisesandlaysafoundationfortheresourceshare,datainheritandCEofthetechnologydepartmentinbusenterprise.ImplementingthesystemwillupgradethetechnologymanagementandmakethebaseoftheCIMSofbusenterprise.
Keywords:Bus,Productdevelopment,ProductDataManagementSystem,Web,ASP
论文题目:热轧带钢轧机工作辊热应力的研究
ThermalStressStudyofWorkRollinHotStripMill
研究生姓名:韩继铖
导师姓名:任学平教授
专业:机械电子工程
摘 要:
热轧带钢轧机工作辊的热变形直接影响着承载辊缝的形状,从而影响着受轧带钢板型质量的好坏.同时工作辊由于受周期性温度的作用,特别是工作辊表面受到瞬态周期性的热冲击,内部产生热应力.在这些周期性热应力的作用下,工作辊表面会产生热疲劳,产生疲劳裂纹而导致工作辊断裂或失效.因此,定性和定量确定热应力显得尤为重要,准确计算工作辊的温度场是计算其热应力的前提.
在工作辊温度场的求解计算中,由于热传导和热变形行为的复杂性,求解工作辊温度场一直是带钢轧制研究领域的薄弱环节.工作辊温度场的求解方法有解析法,数值法和实测法等,但由于热轧工作辊工作条件极其恶劣和复杂,解析法和实测法等都没有令人满意的结果.因此该领域研究重点是数值法,包括差分法和有限元法.本文就是利用ANSYS有限元分析软件对热轧带钢工作辊的温度场和热应力进行解析.在温度场的计算中采用Solid70热单元进行解析,对工作辊施加第三类边界条件载荷,得出工作辊不同时间的ISO方向温度图和温度等高线图,以及工作辊表面不同深度下的温度分布曲线图.在工作辊热应力计算中,采用Solid45结构单元进行解析,把温度作为载荷施加到结构单元上,得到工作辊径向,轴向,剪切方向以及VonMises等效热应力的热应力等值线分布图.
本文还针对某厂2025热轧带钢轧机工作辊进行了计算机仿真,仿真结果与文献中的实验数据有很好的一致性,从而验证了本文模型计算的正确性.其结果可以为板型控制和工作辊寿命计算分析提供理论依据.
关 键 词:工作辊温度场热应力有限元
ABSTRACT
Thethermaldeformationofhotrolledstripworkrollinfluenceddirectlynotonlytheshapeofrollgapbutalsothequalityofstrip.Itwasshownthatthereweregreaterthermalstressformedwithinworkrollwithperiodicaltemperatureimposed,especiallyinstantaneousthermalimpact.Thethermalstressledtothermalfatigueonrollsurface.Asaresult,thefatiguecrackmadetherollbreakanddisable.Therefore,Itwasimportancethatconfirmthethermalstressqualitativelyandquantificationalandtheaccurateputationoftemperaturefieldwasthebaseoftheputationofthermalstress.
Theputationontemperaturefieldofworkrollwasakeybecauseoftheplexityofthermalconductionandthermaldeformationduringhotstriprolling.Thealgorithmincludedanalyticalmethod,numericalmethodandmeasurementmethod,andsoon.Theouteresultedfromanalyticalmethodandmeasurementmethodweredissatisfiedduetothewickedandplicatedworkconditionofworkroll.Soresearchersputanemphasisonthenumericalmethod,whichincludeddifferencemethodandFEM.ThispaperanalyzedtemperaturefieldandthermalstressonthesurfaceofhotrolledstripworkrollerwiththehelpofANSYSsoftware.WeimposedthethirdboundaryconditionloadonworkrollwithSolid70thermalelementresolutionduringputingtemperaturefield.TheresultshowedthatISOdirectiontemperaturechangeswithtime,temperaturecontourline,andtemperaturegraphwithdifferentdepthonthesurfaceofworkroll.Moreover,wegotVonMisesequivalentthermalstresscontourlinegraphinradialdirection,axisdirection,andsheardirectionbyimposingtemperatureloadonstructuralelementwithSolid45structuralelementresolutionduringputingthermalstress.
Ipletedputersimulationof2025hotrolledstripmillworkrollinasteelwork.Theresultaccordedwithactualmeasurementsperfectly,whichprovedtheaccuracyofthesimulationmodel.Theconclusionprovidedananalyticfoundationforstripshapecontrolsandrolllifeputation.
Keywords:Workroll,Temperaturefield,Thermalstress,FEM
材料加工工程
论文题目:快淬Nd-Fe-B永磁体制备工艺与显微组织结构的研究
TheInvestigationsforPreparationTechnologiesand
MicrostructuresofMelt-spunNd-Fe-BPermanentMags
研究生姓名:杨在志
导师姓名:任慧平教授
专业:材料加工工程
摘 要:
近几年来,通过熔体快淬工艺制备的粘结Nd-Fe-B永磁体以容易成型,成本低等优点迅速发展起来,目前在永磁市场中所占的比重逐渐扩大,应用领域已经涉及计算机,汽车,马达,通讯和医疗等领域,成为当今社会信息产业和机电产业的基础材料.但是,粘结永磁体一个缺点就是跟烧结永磁体相比,性能较低.其中一个很重要的原因就是磁粉的性能较低.要制备高性能的粘结永磁体必须要有高性能的磁粉.为了提高粘结永磁体的磁性能,本文主要对熔体快淬制备磁粉工艺和永磁体的模压成型工艺进行了研究.
实验通过熔炼技术,真空快淬技术,真空晶化热处理技术及模压成型技术制备了各向同性的粘结永磁体,使用BH磁滞回线测量仪测量永磁体的磁性能.利用扫描电子显微镜(SEM)观察了永磁合金的组织形貌,分析了晶粒尺寸大小对粘结永磁体磁性能的影响.利用透射电子显微镜(TEM)进行了显微组织分析,确定了在永磁合金的组织中有晶体和非晶共存,通过电子衍射对永磁合金中相的晶体结构进行了分析,同时也研究了非晶组织的转变过程中相的变化对磁性能的影响.在实验中还利用了X衍射仪对永磁合金的晶体取向进行了分析.
实验结果表明:用Pr元素代替NdFeB永磁合金中Nd元素,提高了永磁合金的矫顽力,最大值达到了1227KA/m,熔体真空快淬永磁合金的组成有三部分:非晶区,柱状晶区和等轴晶区.当熔体快淬速度为21m/s时,合金中的柱状晶占大多数,柱状晶的生长具有一定的择优取向,该择优取向和永磁合金中的硬磁相的易磁化方向(C轴)一致,高温短时的晶化热处理工艺可以得到晶粒细小,分布均匀的永磁体晶粒,增加了晶粒的界面积,加强了双相纳米晶复合永磁合金的交换耦合作用,提高永磁体的磁性能.高温真空模压成型工艺提高永磁体密度,减小了孔洞体积率,同时模压的过程中,永磁合金磁粉晶粒会有一定取向&